Ver el documento (formato PDF)   Saleh Medina, Leila María.  "Compositos elastoméricos multiferroicos: aplicaciones en electrónica flexible"  (2016-12-02)
Facultad de Ciencias Exactas y Naturales. Universidad de Buenos Aires
URL:
     
Resumen:
Los materiales multiferroicos poseen simultáneamente al menos dos órdenes ferroicos (por ejemplo, ferromagnético y ferroeléctrico), observándose acoplamiento cruzado entre propiedades. Dicha característica está presente en sistemas monofásicos o multifásicos de varios componentes. Las ferritas de bismuto son cerámicos multiferroicos a temperatura ambiente, si bien es difícil obtenerlas con alta pureza y el acoplamiento magneto-eléctrico suele ser bajo. El primer objetivo de la presente tesis ha sido sintetizar y caracterizar ferritas de bismuto de estequiometría definida (BiFeO3), excelente pureza, y sustituidas parcialmente con itrio como estrategia para modificar los órdenes magnéticos y eléctricos. Se observaron variaciones de las propiedades magnetoeléctricas que se correlacionan con cambios de tamaño de partícula e inducción de nuevas fases. El segundo objetivo fue desarrollar y caracterizar películas flexibles con propiedades dieléctricas que permitan su uso como capacitores multiferroicos para electrónica flexible. Se prepararon compositos flexibles, dados por dispersiones de BiFeO3 en diferentes elastómeros: caucho sintético (SBR, no ferroeléctrico) y difluoruro de polivinilideno (PVDF, ferroeléctrico). Se prepararon películas micrométricas flexibles que presentan altas constantes dieléctricas, ferroelectricidad y acoplamiento magneto-eléctrico. La respuesta dieléctrica se caracterizó en función del contenido de BiFeO3. En SBR estas propiedades se incrementan al preparar los compositos en presencia de campos magnéticos o eléctricos. También se sintetizaron ferritas de cobalto (ferromagnéticas), observándose acoplamiento magneto-eléctrico al ser dispersadas en PVDF. Se demostró que los compositos basados en SBR y PVDF pueden ser empleados como filtros de alta frecuencia en circuitos eléctricos, cuyo comportamiento puede regularse variando el contenido de cerámico.

Abstract:
Multiferroic materials have simultaneously at least two ferroic orders (e.g. ferromagnetic and ferroelectric), that allows cross coupling of properties. This characteristic is present in single-phase or multiphase (made of several components) systems. Bismuth ferrites are multiferroic ceramics at room temperature, although it is difficult to obtain them with high purity and they generally present low magnetoelectric coupling. The main objective of this thesis has been synthesising and characterising bismuth ferrite of defined stoichiometry (BiFeO3), excellent purity and partially substituted with yttrium in order to modify the magnetic and electric structural orders. Changes in magnetoelectric properties, that can be attributed to particle size and new phase induction, have been found. The second objective was to develop and characterise flexible films with dielectric properties that allow their use as multiferroic capacitors for flexible electronics. Flexible composites were prepared by adding BiFeO3 dispersions into different elastomers: synthetic rubber (SBR, non-ferroelectric) and polyvinylidene difluoride (PVDF, ferroelectric). Flexible micrometric films were obtained with large values of dielectric constant, ferroelectricity and magnetoelectric coupling. Dielectric response was characterised as a function of BiFeO3 content. These properties were enhanced in SBR films prepared under the application of electric or magnetic fields. Cobalt ferrites (ferromagnetic) were also synthesised. Magnetoelectric coupling was observed when they were dispersed in PVDF. It has been demonstrated that SBR and PVDF composites can be used as high frequency filters, whose behaviour can be adjusted by modifying the ceramic content.

* A este resumen le pueden faltar caracteres especiales. Consulte la versión completa en el documento en formato PDF

Registro:
Título : Compositos elastoméricos multiferroicos: aplicaciones en electrónica flexible     =    Elastomeric multiferroic composites: applications on flexible electronics
Autor : Saleh Medina, Leila María
Director : Negri, R. Martín
Consejero : Aldabe Bilmes, Sara
Jurados : Hoppe, Cristina E.  ; Kolender, Adriana A.  ; Albores, Pablo
Año : 2016-12-02
Editor : Facultad de Ciencias Exactas y Naturales. Universidad de Buenos Aires
Filiación : Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales
Departamento de Química Inorgánica, Química Analítica y Química Física (DQIAQF)
Instituto de Química Física de los Materiales, Medio Ambiente y Energía (INQUIMAE)
Grado obtenido : Doctor de la Universidad de Buenos Aires en el área de Química Inorgánica, Analítica y Química Física
Ubicación : Preservación - http://digital.bl.fcen.uba.ar/gsdl-282/cgi-bin/library.cgi?a=d&c=tesis&d=Tesis_6124_SalehMedina
Idioma : Español
Area Temática : Química / Química Física
Química / Química de los Materiales
Palabras claves : MATERIALES MULTIFERROICOS; CAPACITORES; EFECTO MAGNETO ELECTRICO; ELECTRONICA FLEXIBLE; BIFEO3; ELASTOMEROS; FERROELECTRICIDAD; MULTIFERROIC MATERIALS; CAPACITORS; MAGNETOELECTRIC EFFECT; FLEXIBLE ELECTRONICS; BIFEO3; FERROELECTRICITY
URL al Documento : 
URL al Registro : 
hola chau _gs.DocumentHeader_ chau2 _documentheader_ chau3
Estadísticas:
     http://digital.bl.fcen.uba.ar
Biblioteca Central Dr. Luis Federico Leloir - Facultad de Ciencias Exactas y Naturales - Universidad de Buenos Aires
Intendente Güiraldes 2160 - Ciudad Universitaria - Pabellón II - C1428EGA - Tel. (54 11) 4789-9293 int 34